HDPE Geomembrane

High Density Polyethylene(HDPE) Geomembrane
smooth

Properties	T est method	Test Value(ave.)
		0.50mm	0.75 mm	1.00mm	1.25mm	1.50mm	2.00mm	2.50mm
Width(mm)	_____	7000	7000	7000	7000	7000	7000	7000
Thickness -mm (min. ave.) L owest individual of 10 values	ASTM D5199	nom. -10%	nom. -10%	nom. -10%	nom. -10%	nom. -10%	nom. -10%	nom. -10%
Density g/cc(min.)	ASTM D1505/D792	0.940	0.940	0.940	0.940	0.940	0.940	0.940
Tensile Properties: Y ield strength break strength Y ield elongation break elongation	ASTM D638 Type IV	10N/mm 16 N/mm 15% 780%	14N/mm 24 N/mm 15% 780%	19N/mm 33N/mm 15% 780%	24N/mm 41 N/mm 15% 780%	29N/mm 50N/mm 15% 780%	38N/mm 66 N/mm 15% 780%	46N/mm 83 N/mm 15% 780%
Tear  Resistance-N	ASTM D1004	75	115	150	190	230	300	375
Puncture Resistance-N	ASTM D4833	240	360	480	590	680	840	950
Stress Crack Resistance	ASTM D5397(APP)	300hr.	300hr.	300hr.	300hr.	300hr.	300hr.	300hr.
Carbon Black Content-%	ASTM D1603 (3)	2.0-3.0%	2.0-3.0%	2.0-3.0%	2.0-3.0%	2.0-3.0%	2.0-3.0%	2.0-3.0%
Carbon Black Dispersion	ASTM D5596	note	note	note	note	note	note	note
Oxidative Induction Time(OIT) (min. ave.) (a)Standard OIT  or (b)High Pressure OIT	ASTM D3895 ASTM D5885	100min. 400min.	100min. 400min.	100min. 400min.	100min. 400min.	100min. 400min.	100min. 400min.	100min. 400min.
Oven Age at 8 5 Standard OIT (min.ave.)-%retained after 90 days	ASTM D5721 ASTM D3895	55%	55%	55%	55%	55%	55%	55%

N ote:1.carbon black dispersion for 10 different views: all 10 in categories 1or 2.

     2.the  table  contents are subject to change without notice.